Quarterly report describing progress on the EVESR Nuclear Superheat Fuel Development Project.

Abstract: Residual and fission gas release from UO2 were studied in the laboratory and in in-reactor experiments. Arc-fused powder and sintered pellets were used to determine the rate of evolution and types of residual gases as a function of temperature. Fission gas release was related to the average UO2 temperature and fission gas release calculations were made using the latest thermal conductivity values, isotopic half lives, and branching ratios available in the literature. The results obtained were compared with those available in the literature, and a satisfactory agreement was found among the groups of comparable data.

Quarterly report discussing progress on the Fast Ceramic Reactor Development Program, "an integrated analytical and experimental program directed toward the development of fast reactors employing ceramic fuels, with particular attention to mixed plutonium-uranium oxide" (p. 1).

The General Electric Company is proceeding with an irradiation program to proof test a representative array of Savannah I fuel rods. Irradiation of a test assembly containing Savannah I fuel rods has begun and it is proposed that the results of this irradiation will permit an advance evaluation of the fuel performance and fuel burnup in the Savannah I reactor. This report covers the first two quarters of the reporting period. All aspects of the subject program have been consolidated and applicable portions are discussed in some detail.

This report contains a listing of the bound-proton kernels for neutron scattering which were calculated in conjunction with the USAEC Control Rod Materials Program.

Abstract: A materials exposure program has been established in the Garigliano Nuclear Power Plant to measure the effect of neutron irradiation and time at temperate on the mechanical properties of the reactor pressure vessel steel. Base metal specimens were made from portions of the pressure vessel steel, and weld heat-affected zone and weld metal samples were taken from a weldment made from the pressure vessel steel and simulating a pressure vessel circumferential weld since there are no longitudinal welds in the forged ring shell. The specimens were sealed in helium-filled capsules and placed in the reactor vessel at locations where they will be exposed to a variety of conditions. Tensile property changes will be measured by pre- and post-irradiation tests on small tensile specimens. Fracture characteristic changes will be measured in similar fashion by Charpy V-notch impact tests. The program is planned to cover a 32-year period, with specimens to be removed for test at intervals of 1, 2, 4, 8, 16, and 32 years.