This research presents the results on an experimental investigation to identify the significant factors influencing horizontal cracking in continuously reinforced concrete pavements (CRCP). An in-depth analysis of the microstructure, morphological characteristics of the interfacial transition zone (ITZ) and the observation of cracking using the environmental scanning electron microscope (ESEM) was done. Characterization of oxides using Fourier transform infrared spectroscopy (FTIR) and electron dispersive x-ray spectroscopy (EDS) was also performed. Water to cement ratio (w/c) and rebar temperature had a significant influence on the rebar-concrete bond strength. The 28-day shear strength measurements showed an increase in rebar-concrete bond strength as the water to cement ratio (w/c) was reduced from 0.50 to 0.40. There was a reduction in the peak pullout load as the temperature increased from 14oF to 252oF for the corroded and non-corroded rebar experiments. The corroded rebar pullout test results showed a 20-50 % reduction in bond strength compared to the non-corroded rebars. FTIR measurements indicated a presence of lepidocrocrite (γ -FeOOH) and maghemite (γ -Fe2O3) on the ITZ. ESEM images showed the existence of microcracks as early as three days after casting with the bridging of these cracks between coarse aggregate locations in the interfacial zone propagating through …

The use of the cold-formed steel sheet bolted connections without washers is so significant; however, the North American Specifications for the Design of Cold Formed Steel Structural Members, NASPEC, doesn't provide provisions for such connections. The bearing failure of sheet and the shear failure of sheet were considered in this study. For the sheet shear strength, it was found that the NASPEC (2007) design provisions can be used for oversized holes in both single and double shear configurations and for the double shear connections on short slotted holes. For the sheet bearing strength, a new design method was proposed to be used for low and high ductile steel sheets. The method was compared with the NASPEC and the University of Waterloo approach. Washers were still required for single shear connections on short slotted holes. Besides, connections using ASTM A325 bolts yielded higher bearing strength than connections using ASTM A307 bolts.