In this paper, I sought to identify and develop a protocol on electrode arrays as a result of rapid aging by applying rapid current over time. We, however, apply a different approach by using phosphate buffer solution (PBS) to mimic the conditions of the body. Here we have established an in vitro protocol for accelerated aging, a process that involves testing in extreme conditions such as oxygen, heat, sunlight, humidity, and vibration aimed at speeding the normal aging process of items; on commercially available shape memory polymer electrode arrays from Qualia over a period of 30 days in PBS. Two electrode arrays were placed in 37°C and 2 were placed in 57°C. Open lead electrochemical impedance spectroscopy (EIS) was conducted on the electrode arrays. Overall, the results showed there were differences in average impedance during this accelerated aging protocol. At 37°C we see that the average impedance values increased as the electrodes were aged at 1kHz from an average of 4.15E6 to 9.14E6 Ohms. At 57°C electrode arrays 4 and 5 showed strong P values well above 0.05, but average impedance increased drastically from 3.27E6 to 9.97E6 and P value of 0.04 from measurement day 24 to day 30. This …

In this research, we aimed to develop thin-film devices on a polymer substrate and an alternative 3D-printed device with macroelectrodes for treating gastrointestinal (GI) conditions. First, the fabrication of thin-film devices was demonstrated on a softening thiol-ene/acrylate polymer utilizing titanium nitride (TiN) as electrode material. This was achieved by utilizing cleanroom fabrication processes such as photolithography, wet and dry etching. The functionality of the device was shown by performing electrochemical characterization tests, mainly cyclic voltammetry, electrochemical impedance spectroscopy, and voltage transient. We synthesized a novel thiol-ene/acrylate polymer based on 1,3,5-triallyl-1,3,5-triazine-2,4,6(1H,3H,5H)-trione (TATATO), trimethylolpropanetris (3-mercaptopropionate) (TMTMP), and polyethylene glycol diacrylate (PEGDA). We show that this stretchable shape memory polymer substrate is well suited for cleanroom processes. Finally, for the high throughput of the wearable devices with electrodes size 10 mm in diameter, we implemented single electrode fabrication using printed circuit boards (PCBs) and depositing gold (Au) and TiN on the plated side of PCBs utilizing the sputtering tool. This step was followed by the assembly of those single electrodes on the flexible 3D printed device. We showed that the TiN electrode material performed better in terms of charge storage capacity and charge injection capacity than the widely used stainless steel electrode material …